Solvent-based primers for furniture

Grinding of a water-based extruder primer for frames
Bucket of solvent-based primer for furniture
Wooden cabinet doors treated with solvent-based primers for furniture

The application of the base coat in furniture painting is a crucial step to ensure a high-quality final result.

They are formulated to provide a uniform base, improve adhesion of subsequent coats, and enhance the aesthetic result of the chosen coating process.

FP 130 polyurethane-based two-component transparent primer is known for its excellent coverage and appreciated for being easily sandable.
CATALYSIS:
catalyzed in a ratio 100:50 weight with C 204
DRYING TIME:
12 hours
OVERCOATING:
with itself after 1 hour or after 12 hours with polyurethane-based products
FP 134 is a two-component, polyurethane-based transparent primer characterized by its thixotropic viscosity. Its special formulation makes it possible to paint vertical surfaces avoiding the problem of dripping. The high-thickness layers can be easily sanded.
CATALYSIS:
catalyzed in a ratio 100:50 weight with C 204
DRYING TIME:
12 hours
OVERCOATING:
with itself after 1 hour or after 12 hours with polyurethane-based products
FA 156 is a transparent two-component acrylic primer. It is appreciated for its high clearness and rapid drying time.
CATALYSIS:
catalyzed in a ratio 100:15 weight with CI 25
DRYING TIME:
8 hours
OVERCOATING:
after 1 hour with itself or after 8 hours with polyurethane-based products
The clear acrylic primer FA 157 is valued both for its thickness and fast drying time. It assures a transparent protection that doesn’t yellow over time.
CATALYSIS:
catalyzed in a ratio 100:15 weight with CI 25
DRYING TIME:
8 hours
OVERCOATING:
after 1 hour with itself or after 8 hours with polyurethane-based products
The FL 226. product line includes two-component, polyurethane-based primers characterized by thixotropic viscosity. They are particularly valued for their special formulation that provides a smooth surface with a
fine-grained satin appearance. FL 226. represents the ideal base for metallic finishes or special applications where a smooth and low absorbent surface is required. FL 226. represents the ideal base for metallic finishes or special applications where a smooth and low absorbent surface is required.
CATALYSIS:
in a ratio 100:50 weight with C 204
DRYING TIME:
8 hours
OVERCOATING:
with itself after 1 hour or after 8 hours with polyurethane-based varnishes
AVAILABLE COLOURS :
FPP 145 is a two-component polyurethane-based clear primer, valued for its high elasticity and excellent filling power. Originally developed for parquet varnishing, it is now widely used in furniture field.
CATALYSIS:
in a ratio 100:100 weight with CI 60
DRYING TIME:
12 hours
OVERCOATING:
with itself after 1 hour or after 12 hours with polyurethane products
The FL 210. product line consists of two-component, polyurethane-based primers available in different colours. They are designed to provide excellent coverage to the painted substrate and be easily sandable.
CATALYSIS:
at a ratio 100:30 weight with C 300
DRYING TIME:
8 hours
OVERCOATING:
after 1 hour with itself or after 8 hours with polyurethane-based products
AVAILABLE COLOURS :
FA 165.100 is a white two-component base coat valued for its excellent surface wettability.
Its application is widely suggested in open pore wood as it guarantees a high definition of pores.
CATALYSIS:
in a ratio 100:20 weight with CI 25
DRYING TIME:
6 hours
OVERCOATING:
with itself or after 6 hours with polyurethane paints
AVAILABLE COLOURS :

Back to products

Choose us for

your

coating

Adding a dye during the production process of a copper-colored paint

Enter the world of Eureka Colour

Discover our wide range of professional and sustainable coatings. Contact us now to discover the world of Eureka Colour. We bring new shades to the life of your wood.